GEMET 702DC

ELECTRODES FOR TIN-BRONZES AND SURFACING.

IDENTIFICATION
Gemet 702 DC, ECuSn-C

CLASSIFICATION
AWS SFA 5.6: E Cu Sn C

DESCRIPTION
A special basic coated electrode for welding and surfacing of copper, brass and bronze. Deposited weld metal is free from porosity. The weld bead is smooth uniform and slag is easy to remove. Weld metal has higher hardness and higher tensile strength & yield strength compared to ECuSnA electrodes.
ALLOY BASIS : Cu, Sn, P

WELD METAL ANALYSIS (RANGE) %

Sn P Al Zn Fe Pb
7.0 - 9.0 0.10 - 0.35 0.01 max 0.20 max 0.10 max 0.02 max

MECHANICAL PROPERTIES (RANGE)

UTS (MPa) EL (%) (L=4D) Hardness of the Weld Metal
300 - 550 20 % approx. 70 - 90 Brinell

TYPICAL APPLICATIONS

  • Welding tin bronze (Phosphor bronzes)
  • Bell metal (Cu + 20-25% Zn)
  • Brasses
  • Manganese Bronzes, pump impellers
  • For welding copper base alloys to themselves and to steels or cast irons.
  • To weld overlays shafts and engineering components to give a bearing surface and or corrosion resistant layer.
  • For joining phosphorus bronzes of similar composition.
  • Joining for brasses

PROCEDURE

Prepare large “V” approximately 80 - 90º. Preheat to 300ºC to reduce sluggish behaviour of weld pool.

REDRY : Redry if moist at 250 - 300ºC for 1 -2 hrs.

WELDING CURRENT : DC (+)

PACKING PARAMETERS

Size (mm) Length (mm) Current Condition DC (+) Amps Packing / Packet (kg) Packing / Box (kg)
2.5 350 60 - 90 2 2 x 5 = 10
3.15 / 3.20 350 75 - 120 2 2 x 5 = 10
4 350 100 - 160 2 2 x 5 = 10