IDENTIFICATION
GRIBINOX 410 E410-15
CLASSIFICATION
AWS/SFA 5.4: E410-15
DESCRIPTION
A basic coated hydrogen controlled electrode manufactured using alloyed core wire designed for welding wrought or cast martensitic (12% Cr type 410) stainless steel. The weld metal contains just sufficient carbon to enable air hardening transformation to a predominantly martensitic microstructure. The electrode exhibits good erosion and abrasion resistance. It deposits weld metal of X-ray quality.
WELD METAL ANALYSIS (RANGE) %
| C | Mn | Si | Cr | Ni | Mo | S | P |
| 0.12 max | 0.40 - 0.80 | 0.25 - 0.60 | 11.5 - 14.0 | 0.60 max | 0.75 max | 0.03 max | 0.04 max |
MECHANICAL PROPERTIES (RANGE)
| TS (MPa) | YS (MPa) | EL (%) (L=4D) |
| 500 min | 400 -450 | 28 min |
After PWHT, 730 - 760°C / 1 hr. Furnace Cool to 315°C, then air cool.
TYPICAL APPLICATIONS
Cast valve bodies, turbine parts, burner nozzles, run-out rolls in steel mills, hydrocracker reaction vessels, furnace parts suitable for surfacing mild and low alloy steels.
DRYING OF ELECTRODES : 250 – 300°C / 2 hrs
MOISTURE IN THE FLUX COATING : 0.3% by weight, maximum
DIFFUSIBLE HYDROGEN CONTENT IN THE WELD METAL : Max 4 ml/100 g
WELDING POSITION :
PACKING PARAMETERS
| Size (mm) | Length (mm) | AMPS AC / DC (+) | Packing / Box (kg) | Packing / Box (Pcs) |
| 2.5 | 350 | 60 - 90 | 2 x 5 = 10 | 94 x 5 = 470 |
| 3.15 / 3.20 | 350 | 80 - 130 | 2 x 5 = 10 | 60 x 5 = 300 |
| 4 | 350 | 130 - 160 | 2 x 5 = 10 | 38 x 5 = 190 |
| 5 | 350 | 160 - 230 | 2 x 5 = 10 | 24 x 5 = 120 |