IDENTIFICATION
GRILOY 43N E430-15
CLASSIFICATION
AWS/SFA 5.4 E430-15
DESCRIPTION
A basic coated hydrogen controlled electrode manufactured using alloyed core wire depositing weld metal having low carbon and about 17% Chromium. The weld metal consists of ferrite and some martensite in the as welded condition. In order to avoid excessive grain growth, the interpass temperature should not exceed 300°C. The deposited weld metal is of X-ray quality.
WELD METAL ANALYSIS (RANGE) %
| C | Mn | Si | Cr | Ni | Mo | S | P | Cu |
| 0.10 max | 0.25 - 0.90 | 0.25 - 0.65 | 15 - 18 | 0.60 max | 0.75 max | 0.03 max | 0.04 max | 0.3 max |
MECHANICAL PROPERTIES (RANGE)
| TS (N/mm2) | EL (%) (L=4D) |
| 460 - 640 | 20 - 26 |
After PWHT, 760 - 790°C / 2 hr. Furnace cool to 600°C at 55°C / hr max, then air cool to room temp
TYPICAL APPLICATIONS
Surfacing valves, suitable for welding Cr-Si-Al steels (Sicranals) with upto 18% Cr used for furnace parts, exhaust ducting’s, petrochemical and steam generating industries. AISI 430, DIN 1.4013, 1.4015, and 1.4016.
HARDNESS OF THE WELD METAL : 200 – 280 HV10
ASME IX QUALIFICATION : QW -432 F-NO. 4, QW-442 A-NO. 7
MICROSTRUCTURE : In the PWHT condition, the microstructure consists of ferrite and tempered marten site with some chromium carbide.
REDRYING : 300°C / 2 hrs. 5 cycles, 10 hrs total max.
WELDING POSITION :
PACKING PARAMETERS
| Size (mm) | Length (mm) | AMPS AC / DC (+) | Packing / Box (kg) | Packing / Box (Pcs) |
| 2.5 | 350 | 70 - 100 | 2 x 5 = 10 | 94 x 5 = 470 |
| 3.15 / 3.20 | 350 | 80 - 125 | 2 x 5 = 10 | 60 x 5 = 300 |
| 4 | 350 | 120 - 180 | 2 x 5 = 10 | 38 x 5 = 190 |
| 5 | 350 | 160 - 240 | 2 x 5 = 10 | 24 x 5 = 120 |