IDENTIFICATION
GRITINOX 317L E317L–17
CLASSIFICATION
AWS/SFA 5.4: E317L-17
DESCRIPTION
A titania coated stainless steel electrode depositing low carbon 18/13/3.5 Mo austenitic stainless steel weld metal. Deposited weld metal has very high resistance to hot cracking, chemical corrosion upto 800°C and stress corrosion cracking. Molybdenum imparts resistance to corrosion of reducing nature. The deposited weld metal is of radiographic quality.
WELD METAL ANALYSIS (RANGE) %
| C | Mn | Si | S | P | Cr | Ni | Mo | Cu |
| 0.04 max | 0.50 - 2.50 | 1.0 max | 0.03 max | 0.04 max | 18.0 - 20.0 | 12.0 - 14.0 | 3.0 - 4.0 | 0.75 max |
MECHANICAL PROPERTIES (RANGE)
| UTS (MPa) | EL (%) (L=4D) | CVN Impact Value | |
| Temp | Joules | ||
| 520 min | 30 min | 27°C | 70 min |
TYPICAL APPLICATIONS
• Suitable for welding stainless steels extra low carbon or stabilised by Titanium or Niobium such as AISI grades 317L and 318, S.S. clad pleas, chemical plants, pain and dye industries.
• For welding stainless steel represented by AISI grades 316L, 317L & 318.
FERRITE CONTENT IN THE WELD METAL : 3 to 9 FN
REDRYING : 250°C / 2 hrs, max 5 cycles, 10 hr. total.
WELDING POSITION :
PACKING PARAMETERS
| Size (mm) | Length (mm) | AMPS AC / DC (+) | Packing / Box (kg) | Packing / Box (Pcs) |
| 2.5 | 350 | 60 – 80 | 2 x 5 = 10 | 94 x 5 = 470 |
| 3.15 / 3.20 | 350 | 80 – 110 | 2 x 5 = 10 | 60 x 5 = 300 |
| 4 | 350 | 110 - 140 | 2 x 5 = 10 | 38 x 5 = 190 |
| 5 | 350 | 140 - 180 | 2 x 5 = 10 | 24 x 5 = 120 |